LORD 410/19 GB
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- Acrylic Metal/Engineered-Plastic Structural Adhesive
- 20 to 30-Minute Working Window
- 18.6 MPa Cured Tensile Strength
Product Description
LORD® 410 Acrylic Adhesive is a two-component acrylic structural adhesive used with LORD Accelerator 17, 19, or 19GB to bond prepared or unprepared metals and engineered plastics. The non-sag adhesive component has a typical viscosity of 100,000 to 300,000 cP at 25°C. When mixed with a recommended accelerator, the LORD 410 system provides a typical working time of 20 to 30 minutes, handling strength in 60 to 120 minutes, and full cure in 24 hours at 24°C. Typical cured properties with Accelerator 19 include 18.6 MPa tensile strength and 30% elongation.
Key features
- Multi-substrate structural bonding: The adhesive system is documented for metals and engineered plastics.
- 20 to 30-minute working time: The mixed LORD 410 system provides handling strength in 60 to 120 minutes at 24°C.
- Accelerator options: Accelerators 17, 19, and 19GB support different mix ratios and processing configurations.
Applications / Suitable for
- Bonding prepared or unprepared metals
- Bonding XENOY, polycarbonate, ABS, and acrylic plastics
- Assemblies requiring impact and peel resistance
TDS, SDS & Technical Documents
Technical Specifications
No specifications available.
Additional Information
As-supplied / before-processing properties
Typical as-supplied or mixed-state values unless otherwise stated. These values are not sales specifications.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Appearance | Off-white to tan paste | N/A | LORD 410 adhesive component |
| Viscosity | 100,000 to 300,000 | cP | Brookfield at 25°C |
| Density | 1,096 to 1,156 | kg/m³ | As supplied |
| Working time | 20 to 30 | min | Mixed with recommended accelerator at 24°C |
| Time to handling strength | 60 to 120 | min | 50 psi shear at 24°C |
| Full cure | 24 | h | At 24°C |
After-processing / final-state properties
Typical final-state values under the stated system and test conditions. These values are not sales specifications.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Tensile strength | 18.6 | MPa | LORD 410 with Accelerator 19; ASTM D638 modified |
| Elongation | 30 | % | LORD 410 with Accelerator 19; ASTM D638 modified |
| Young's modulus | 896.3 | MPa | LORD 410 with Accelerator 19; ASTM D638 modified |
| Glass-transition temperature | 72 | °C | LORD 410 with Accelerator 19; ASTM E1640-99 by DMA |
| Service temperature | -40 to 149 | °C | Documented adhesive-system range |